  • Specification of Required Raw Material for Making Bricks

    brick-raw-material


    1. Chemical Composition

    Chemical Required data Explanation
     
    SiO2
     
     
    55~70% Raw material with bigger particle of SiO2  can improve bricks refractoriness, 
    reduce the shrinkage and sensitivity when drying; Raw material with smaller 
    particle of SiO2  can let the structure of bricks even and dense. 
    But if the SiO2 is more than 80%, the final finished bricks are easy expansion 
    and the bending strength will be reduced. If less than 45%, 
    the performance of frost resisting is bad.
    Fe2O3 2-10% It effects the color of bricks. If the raw material with bigger particle of Fe2O3, 
    there will be brown or black spot on (or in) bricks.
    Al2O3 10~25% It effects the mechanical strength of bricks. If the content of Al2O3  is more than 20%, 
    the mechanical strength will improve, but the burning temperature will increase; 
    if it is less than 10%, the mechanical strength will reduce.
    CaO <10% It is a kind of co-solvent to reduce the refractory degree. 
    If the particle size of CaO is more than 1mm, there will be lime crack for bricks.
    MgO <5% It is also a kind of co-solvent to reduce the refractory degree. 
    But it is not obvious like CaO. 
    The MgSO in raw material can let the bricks occur scum.
    LOI 6-8% It is the weight percent of lost when the dried (in 105-110℃) raw material burning in 1000-1100℃ . 
    It shows the content of products in gas state (H2O, CO2) 
    and organic material after the raw material is fired and decomposed, 
    then judge whether to pre-burn it or not to let the volume of raw material stable.

    2. Physical Performance

    2.1 Particle composition
    The particle size of raw material will effect directly on the plasticity, drying shrinkage, burning shrinkage, void ratio of bricks.
    The particle size can be graded into three levels:>0.02mm, 0.02-0.002mm, <0.002mm.
    There should be suitable proportion for the three grades particle in raw material to make bricks as follows:
     
      >0.02mm 0.02-0.002mm <0.002m
    Allowed range 10~50 40~80 2~28
    Suitable range 15~30 45~60 5~25
    Remarks There is no sticky performance 
    if the particle size is more than 0.02mm. 
    It has the effect of skeleton 
    when drying and burning. If less 
    0.02mm in raw material, 
    easy to mold, burning temperature low, 
    but difficult to dry
    There is some sticky performance 
    if the particle size is between 0.02-0.002mm, 
    it has the effect of skeleton and filling.
    There is much sticky performance 
    if the particle size is less than 0.002mm, 
    can occur plasticity when meet water. 
    This part of particle in raw material is 
    essential but can not be more, 
    or it will be difficult to dry.


    2.2 Physical performance
    Physical performance Required data Remarks
    Plasticity index 7~15% It is the data (Liquid limit –Plastic limit)
    Shrinkage   The shrinkage data will effect the speed of drying, when data is more, 
    had better to slow down the speed of drying, or the bricks will be easy 
    to crack to effect the quality of bricks.
    Sensitivity    The data of plasticity is high, the dried linear shrinkage rate and dried 
    sensitivity will be high 
     

    Nepal-Clay
    Clay

    fly-ash
    Fly Ash

    coal-gangue
    Coal Gangue

    shale
    Shale

    sludge
    Sludge